Aluminum Trifluoride (ideal gas)	AlF3(g)	Al1F3(g)	Pankratz 1984 (B674)	[Formation: Al(c,l) + 1.5F 2 (g) = AlF 3 (g)]			
T(K)	Cp (J/mol*K)	S (J/mol*K)	-[G-H(Tr)]/T (J/mol*K)	H-H(Tr) (kJ/mol*K)	delta-f H (kJ/mol*K)	delta-f G (kJ/mol*K)	log Kf
298.15	62.530	276.772	276.772	0.000	-1210.850	-1194.268	209.229
300	62.664	277.161	276.772	0.117	-1210.866	-1194.168	207.921
400	68.626	296.060	279.311	6.699	-1211.611	-1188.482	155.198
500	72.601	311.834	284.286	13.774	-1212.193	-1182.633	123.547
600	75.249	325.319	290.027	21.175	-1212.724	-1176.666	102.437
700	77.061	337.063	295.922	28.798	-1213.276	-1170.608	87.351
800	78.337	347.439	301.725	36.572	-1213.921	-1164.474	76.031
900	79.258	356.724	307.336	44.451	-1214.691	-1158.248	67.222
933.61	79.488	359.636	309.164	47.120	-1214.983	-1156.135	64.684
933.61	79.488	359.636	309.164	47.120	-1225.778	-1156.135	64.684
1000	79.944	365.113	312.700	52.413	-1226.268	-1151.173	60.130
1100	80.467	372.757	317.812	60.438	-1226.979	-1143.625	54.306
1200	80.873	379.777	322.691	68.505	-1227.682	-1136.019	49.449
1300	81.195	386.263	327.331	76.609	-1228.368	-1128.345	45.337
1400	81.454	392.292	331.762	84.743	-1229.058	-1120.634	41.811
1500	81.663	397.915	335.984	92.897	-1229.749	-1112.865	38.753
1600	81.839	403.191	340.021	101.073	-1230.431	-1105.045	36.076
1700	81.981	408.158	343.883	109.265	-1231.113	-1097.183	33.712
1800	82.107	412.848	347.586	117.470	-1231.811	-1089.288	31.610
1900	82.211	417.291	351.142	125.683	-1232.502	-1081.346	29.728
2000	82.299	421.509	354.552	133.909	-1233.205	-1073.376	28.033